High-Temperature Oxidation and Oxide Scale Formation in Plasma-Sprayed CoNiCrAlYRe Coatings

TitoloHigh-Temperature Oxidation and Oxide Scale Formation in Plasma-Sprayed CoNiCrAlYRe Coatings
Tipo di pubblicazioneArticolo su Rivista peer-reviewed
Anno di Pubblicazione2014
AutoriDi Girolamo, G., Brentari A., Blasi C., Pilloni L., and Serra Emanuele
RivistaMetallurgical and Materials Transactions A: Physical Metallurgy and Materials Science
Volume45
Paginazione5362-5370
ISSN10735623
Parole chiaveAluminum, Atmospheric plasma spraying, Energy dispersive spectroscopy, Environmental resistance, High temperature, High-temperature exposure, Low oxygen contents, MCrAlY coatings, Ni-based superalloys, Plasma jets, Plasma spraying, Plasma-sprayed, Scale (deposits), Scanning electron microscopy, Sprayed coatings, X ray diffraction
Abstract

MCrAlY coatings are usually adopted to improve the environmental resistance of Ni-based superalloy components of turbine engines against high-temperature oxidation and hot corrosion. In this work, CoNiCrAlYRe coatings were produced by atmospheric plasma spraying. The coatings exhibited relatively low oxygen content and porosity. X-ray diffraction, scanning electron microscopy, and energy dispersive spectroscopy analyses revealed that the high-temperature exposure at 1383 K (1110 °C) promoted the growth of an oxide scale on the top surface being composed of a continuous and dense Al2O3 inner layer followed by an outer mixed layer (Cr2O3 and spinels). The oxide scale was mainly composed of Al2O3, while the formation of mixed oxides occurred at lesser extent. After high-temperature exposure, the formation of internal oxides in some areas reduced the inter-lamellar cohesion, so that a decrease in microhardness was found. © 2014, The Minerals, Metals & Materials Society and ASM International.

Note

cited By 0

URLhttps://www.scopus.com/inward/record.uri?eid=2-s2.0-84920252450&doi=10.1007%2fs11661-014-2509-5&partnerID=40&md5=a77d77a2176dc48560162d383814a0bd
DOI10.1007/s11661-014-2509-5
Citation KeyDiGirolamo20145362